Norwegian scientists have used varied imaging and characterization methods to investigate cells and different elements of silicon PV modules which have been put in within the discipline for greater than 10 years. The objective of the group is to isolate the function of moisture within the completely different mechanisms that trigger the lack of efficiency over time, and to know how these mechanisms develop within the long-term set up of the true exterior circumstances.

Making elements that may face up to outside set up for years and even many years, in any kind of local weather, whereas sustaining not less than most of their preliminary efficiency, is a key objective for photo voltaic. trade.

There have been many developments, with each technological progress and competitors between producers driving greater product and efficiency ensures, and due to this fact longer contracts for the sale of electrical energy from one photo voltaic mission. Most producers now supply 30-year ensures that assure not less than 80% of the preliminary efficiency of the modules, and one even extends it as much as 40 years.

However for photo voltaic installations many areas are focused, for 2050 and past, even longer life is required, particularly for installations situated in troublesome local weather areas even due to warmth, chilly, humidity, mud or different circumstances. And this implies understanding precisely how PV modules are likely to degrade below these circumstances.

Scientists led by the College of Agder in Norway determined to deal with deterioration on account of humidity – that is the principle attribute of the local weather in Grimstad the place the college is predicated.

The workforce took modules from a decommissioned PV array put in within the city in 2000 and used quite a lot of methods, each non-destructive and damaging, to look at the internal workings of the modules, and the way the completely different elements have occurred over time within the discipline.

Their outcomes are described in full within the paper “Moisture induced degradation in field-aged multicrystalline silicon photovoltaic modules,” revealed in Photo voltaic Power Supplies and Photo voltaic Cells. The examine discovered that moisture ingress causes the deterioration of the encapsulant, producing acetic acid and varied substances that promote corrosion and different varieties of degradation of silicon cells. Moisture has additionally been discovered to play a significant function within the corrosion of solder joints – inflicting result in corrosion slightly than the “sacrificial” tin connected to the solder.

The scientists behind the work acknowledge that PV supplies and manufacturing processes have improved considerably for the reason that modules on this examine had been developed greater than 20 years in the past. Nonetheless, whereas accelerated testing is helpful, they are saying that learning modules with age within the discipline remains to be wanted, and most of the mechanisms revealed on this examine are nonetheless related to modules working on manufacturing strains. right this moment.

“Though photo voltaic PV module supplies and expertise have advanced over time, the MID mechanisms of photo voltaic PV modules seem to observe the identical development,” they stated within the paper. “Subsequently, the insights from this work can information present and future decision-making relating to understanding the efficiency reliability of photo voltaic PV vegetation.”